KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.17 – 0.23 |
max 0.4 |
0.65 – 0.95 |
max 0.025 |
0.02 – 0.04 |
0.35 – 0.7 |
0.15 – 0.25 |
0.4 – 0.7 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
20NiCrMoS2-2 |
20NiCrMoS2-2 |
20NiCrMoS2-2 |
20NiCrMoS2-2 |
20NiCrMoS2-2 |
20NiCrMoS2-2 |
20NiCrMoS2-2 |
Mekanik Özellikler |
Sertlik için üretilmiş |
~ 3 mm |
37 – 44 HRC |
|
|
|
|
|
|
|
~ 7 mm |
25 – 36 HRC |
|
|
|
|
|
|
|
~ 11 mm |
20 – 29 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 26 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 21 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 20 HRC |
|
|
|
|
|
|
|
Suverilmiş ve menevişlenmiş at ~ 200 ° C |
16 – 40 mm |
>= 800 MPa |
|
|
|
|
|
|
1) |
~ 3 mm |
37 – 48 HRC |
|
|
|
|
|
|
|
~ 7 mm |
25 – 42 HRC |
|
|
|
|
|
|
|
~ 11 mm |
20 – 33 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 30 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 25 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 24 HRC |
|
|
|
|
|
|
|
~ 3 mm |
41 – 48 HRC |
|
|
|
|
|
|
|
~ 7 mm |
31 – 42 HRC |
|
|
|
|
|
|
|
~ 11 mm |
24 – 33 HRC |
|
|
|
|
|
|
|
~ 15 mm |
21 – 30 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 25 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 24 HRC |
|
|
|
|
|
|
|
~ 3 mm |
37 – 44 HRC |
|
|
|
|
|
|
|
~ 7 mm |
25 – 36 HRC |
|
|
|
|
|
|
|
~ 11 mm |
20 – 29 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 26 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 21 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 20 HRC |
|
|
|
|
|
|
|
Barlar |
10 – 40 mm |
149 – 194 HB |
|
|
|
|
|
|
|
5 – 10 mm |
<= 570 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 62 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 710 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 57 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 610 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 60 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 590 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 60 % |
|
|
|
|
|
|
|
Tel |
5 – 10 mm |
<= 570 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 62 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 710 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 57 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 610 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 60 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 590 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 60 % |
|
|
|
|
|
|
|
|