KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.17 – 0.23 |
max 0.4 |
0.7 – 1 |
max 0.025 |
0.02 – 0.04 |
0.3 – 0.6 |
0.4 – 0.5 |
0.00 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
20MoCrS4 |
8660 |
20MoCrS4 |
20MoCrS4 |
20MoCrS4 |
20MoCrS4 |
20MoCrS4 |
Mekanik Özellikler |
Sertlik için üretilmiş |
~ 3 mm |
37 – 44 HRC |
|
|
|
|
|
|
|
~ 7 mm |
27 – 36 HRC |
|
|
|
|
|
|
|
~ 11 mm |
22 – 31 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 27 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 22 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 20 HRC |
|
|
|
|
|
|
|
16 – 40 mm |
>= 800 MPa |
|
|
|
|
|
|
1) |
kesmeye hazır halde |
~ 3 mm |
37 – 47 HRC |
|
|
|
|
|
|
|
~ 7 mm |
27 – 41 HRC |
|
|
|
|
|
|
|
~ 11 mm |
22 – 35 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 31 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 26 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 24 HRC |
|
|
|
|
|
|
|
~ 3 mm |
40 – 47 HRC |
|
|
|
|
|
|
|
~ 7 mm |
32 – 41 HRC |
|
|
|
|
|
|
|
~ 11 mm |
26 – 35 HRC |
|
|
|
|
|
|
|
~ 15 mm |
22 – 31 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 26 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 24 HRC |
|
|
|
|
|
|
|
~ 3 mm |
37 – 44 HRC |
|
|
|
|
|
|
|
~ 7 mm |
27 – 36 HRC |
|
|
|
|
|
|
|
~ 11 mm |
22 – 31 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 27 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 22 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 20 HRC |
|
|
|
|
|
|
|
10 – 40 mm |
140 – 187 HB |
|
|
|
|
|
|
|
5 – 10 mm |
<= 540 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 62 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 660 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 57 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 580 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 60 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 560 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 60 % |
|
|
|
|
|
|
|
Tel |
5 – 10 mm |
<= 540 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 62 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 660 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 57 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 580 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 60 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 560 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 60 % |
|
|
|
|
|
|
|
|