KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.15 – 0.21 |
max 0.4 |
0.6 – 0.9 |
max 0.025 |
0.02 – 0.04 |
0.9 – 1.2 |
0.15 – 0.25 |
0.00 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
18CrMoS4 |
18CrMoS4 |
18CrMoS4 |
18CrMoS4 |
18CrMoS4 |
18CrMoS4 |
18CrMoS4 |
Mekanik Özellikler |
Sertlik için üretilmiş |
~ 3 mm |
37 – 43 HRC |
|
|
|
|
|
|
|
~ 7 mm |
30 – 38 HRC |
|
|
|
|
|
|
|
~ 11 mm |
24 – 33 HRC |
|
|
|
|
|
|
|
~ 15 mm |
21 – 30 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 25 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 23 HRC |
|
|
|
|
|
|
|
16 – 40 mm |
>= 900 MPa |
|
|
|
|
|
|
1) |
~ 3 mm |
37 – 46 HRC |
|
|
|
|
|
|
|
~ 7 mm |
30 – 42 HRC |
|
|
|
|
|
|
|
~ 11 mm |
24 – 37 HRC |
|
|
|
|
|
|
|
~ 15 mm |
21 – 34 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 29 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 27 HRC |
|
|
|
|
|
|
|
~ 3 mm |
40 – 46 HRC |
|
|
|
|
|
|
|
~ 7 mm |
34 – 42 HRC |
|
|
|
|
|
|
|
~ 11 mm |
28 – 37 HRC |
|
|
|
|
|
|
|
~ 15 mm |
25 – 34 HRC |
|
|
|
|
|
|
|
~ 25 mm |
20 – 29 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 27 HRC |
|
|
|
|
|
|
|
~ 3 mm |
37 – 43 HRC |
|
|
|
|
|
|
|
~ 7 mm |
30 – 38 HRC |
|
|
|
|
|
|
|
~ 11 mm |
24 – 33 HRC |
|
|
|
|
|
|
|
~ 15 mm |
21 – 30 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 25 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 23 HRC |
|
|
|
|
|
|
|
10 – 40 mm |
140 – 187 HB |
|
|
|
|
|
|
|
5 – 10 mm |
<= 530 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 62 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 650 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 57 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 570 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 60 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 550 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 60 % |
|
|
|
|
|
|
|
Tel |
5 – 10 mm |
<= 530 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 62 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 650 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 57 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 570 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 60 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 550 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 60 % |
|
|
|
|
|
|
|
|