KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.14 – 0.19 |
max 0.4 |
1 – 1.3 |
max 0.025 |
max 0.035 |
0.8 – 1.1 |
0.00 |
0.00 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
16MnCr5 |
5117 |
16MnCr5 |
16 MC 5 |
16 MnCr 5 |
15CrMn |
16MnCr5 |
Mekanik Özellikler |
Sertlik için üretilmiş |
~ 3 mm |
39 – 46 HRC |
|
|
|
|
|
|
|
~ 7 mm |
32 – 41 HRC |
|
|
|
|
|
|
|
~ 11 mm |
26 – 37 HRC |
|
|
|
|
|
|
|
~ 15 mm |
22 – 33 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 30 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 28 HRC |
|
|
|
|
|
|
|
~ 3 mm |
36 – 43 HRC |
|
|
|
|
|
|
|
~ 7 mm |
28 – 37 HRC |
|
|
|
|
|
|
|
~ 11 mm |
21 – 32 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 28 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 25 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 23 HRC |
|
|
|
|
|
|
|
16 – 40 mm |
>= 900 MPa |
|
|
|
|
|
|
1) |
~ 3 mm |
36 – 46 HRC |
|
|
|
|
|
|
|
~ 7 mm |
28 – 41 HRC |
|
|
|
|
|
|
|
~ 11 mm |
21 – 37 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 33 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 30 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 28 HRC |
|
|
|
|
|
|
|
~ 3 mm |
39 – 46 HRC |
|
|
|
|
|
|
|
~ 7 mm |
32 – 41 HRC |
|
|
|
|
|
|
|
~ 11 mm |
26 – 37 HRC |
|
|
|
|
|
|
|
~ 15 mm |
22 – 33 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 30 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 28 HRC |
|
|
|
|
|
|
|
~ 3 mm |
36 – 43 HRC |
|
|
|
|
|
|
|
~ 7 mm |
28 – 37 HRC |
|
|
|
|
|
|
|
~ 11 mm |
21 – 32 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 28 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 25 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 23 HRC |
|
|
|
|
|
|
|
10 – 40 mm |
140 – 187 HB |
|
|
|
|
|
|
|
5 – 10 mm |
<= 530 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 64 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 650 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 59 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 570 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 62 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 550 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 62 % |
|
|
|
|
|
|
|
Tel |
5 – 10 mm |
<= 530 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 64 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 650 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 59 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 570 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 62 % |
|
|
|
|
|
|
|
10 – 40 mm |
<= 550 MPa |
|
|
|
|
|
|
|
10 – 40 mm |
>= 62 % |
|
|
|
|
|
|
|
|
Mekanik Özellikler |
su verilmiş |
~ 3 mm |
36 – 46 HRC |
|
|
|
|
|
|
|
~ 7 mm |
26 – 41 HRC |
|
|
|
|
|
|
|
~ 11 mm |
21 – 37 HRC |
|
|
|
|
|
|
|
~ 15 mm |
<= 33 HRC |
|
|
|
|
|
|
|
~ 25 mm |
<= 30 HRC |
|
|
|
|
|
|
|
~ 35 mm |
<= 28 HRC |
|
|
|
|
|
|
|
~ 40 mm |
<= 27 HRC |
|
|
|
|
|
|
|
Boru |
tavlı |
Sertlik [HB 30] |
boyut |
değer |
|
|
|
|
|
|
|
|
<= 207 HB 30 |
|
|
|
|
|
|
|
Sertlik için üretilmiş |
Sertlik [HB 30] |
boyut |
değer |
|
|
|
|
|
|
|
|
156 – 207 HB 30 |
|
|
|
|
|
|
|
ferit-perlit mikro ve sertlik aralığı + parlak dönüşler için çelikler |
Sertlik [HB 30] |
boyut |
değer |
|
|
|
|
|
|
|
|
140 – 187 HB 30 |
|
|
|
|
|
|
|
|