Ürün Materyel No
1.4362
Ürün Adı
X2CrNiN23-4

KİMYASAL BİLEŞİM

C Si Mn P S Cr Mo Ni V
max 0.03 max 1 max 2 max 0.035 max 0.015 22 – 24 0.1 – 0.6 3.5 – 5.5 0.00
Al Cu Pb N Ti Br Sc Bh Sn
0.00 0.1 – 0.6 0.00 0.05 – 0.2 0.00 0.00 0.00 0.00 0.00

STANDARTLARIN KARŞILAŞTIRILMASI

Avrupa
EURO
Almanya
DIN
Amerika
AISI-SAE
Fransa
AFNOR
İtalya
UNI
Çin
GB
Türkiye
TSE
X2CrNiN23-4 S32304 X2CrNiN23-4 Z 3 CN 23-04 Az X2CrNiN23-4 X2CrNiN23-4 X2CrNiN23-4
Mekanik Özellikler
Çözelti ile ısıl işlem görmüş
<= 3 mm >= 25 % enine ~ 20 ° C 2)
4)
<= 3 mm >= 25 % enine ~ 20 ° C 5)
<= 50 mm >= 120 J boyuna ~ 20 ° C
<= 13.5 mm >= 400 MPa enine ~ 20 ° C 7)
3 – 13.5 mm >= 20 % enine ~ 20 ° C
<= 3 mm >= 20 % enine ~ 20 ° C 2)
4)
<= 3 mm >= 20 % enine ~ 20 ° C 5)
<= 13.5 mm >= 120 J boyuna ~ 20 ° C
<= 8 mm >= 420 MPa enine ~ 20 ° C 7)
3 – 8 mm >= 20 % enine ~ 20 ° C
<= 3 mm >= 20 % enine ~ 20 ° C 2)
4)
<= 3 mm >= 20 % enine ~ 20 ° C 5)
<= 8 mm >= 120 J boyuna ~ 20 ° C
>= 300 MPa ~ 150 ° C
>= 265 MPa ~ 250 ° C
Sıcak haddelenmiş levha
>= 3 mm >= 25 % enine ~ 20 ° C
<= 3 mm >= 25 % enine ~ 20 ° C 2)
3)
<= 3 mm >= 25 % enine ~ 20 ° C 4)
>= 10 mm >= 60 J enine ~ 20 ° C
Sıcak haddelenmiş şerit
>= 3 mm >= 20 % enine ~ 20 ° C
<= 3 mm >= 20 % enine ~ 20 ° C 2)
3)
<= 3 mm >= 20 % enine ~ 20 ° C 4)
>= 10 mm >= 60 J enine ~ 20 ° C
soğuk haddelenmiş şerit
>= 3 mm >= 20 % enine ~ 20 ° C
<= 3 mm >= 20 % enine ~ 20 ° C 2)
3)
<= 3 mm >= 20 % enine ~ 20 ° C 4)
Mekanik Özellikler
Barlar
>= 300 MPa ~ 150 ° C
>= 265 MPa ~ 250 ° C
>= 300 MPa ~ 150 ° C
>= 265 MPa ~ 250 ° C
>= 0.05 mm 900 – 1,100 MPa 9)
13)
>= 0.05 mm 1,100 – 1,350 MPa 3)
13)
>= 0.05 mm 1,400 – 1,700 MPa 5)
13)
>= 0.05 mm 1,800 – 2,100 MPa 7)
13)
Kangal
>= 300 MPa ~ 150 ° C
>= 265 MPa ~ 250 ° C
1 – 3 mm <= 1,000 MPa ~ 20 ° C 1)
12)
5 – 16 mm <= 900 MPa ~ 20 ° C 1)
12)
1 – 3 mm >= 20 % ~ 20 ° C 12)
5 – 16 mm >= 25 % ~ 20 ° C 12)
>= 300 MPa ~ 150 ° C
>= 265 MPa ~ 250 ° C
>= 3 mm >= 25 % enine ~ 20 ° C
<= 3 mm >= 25 % enine ~ 20 ° C 2)
3)
<= 3 mm >= 25 % enine ~ 20 ° C 4)
>= 10 mm >= 60 J enine ~ 20 ° C
Sıcak haddelenmiş şerit
>= 3 mm >= 20 % enine ~ 20 ° C
<= 3 mm >= 20 % enine ~ 20 ° C 2)
3)
<= 3 mm >= 20 % enine ~ 20 ° C 4)
>= 10 mm >= 60 J enine ~ 20 ° C
soğuk haddelenmiş şerit
>= 3 mm >= 20 % enine ~ 20 ° C
<= 3 mm >= 20 % enine ~ 20 ° C 2)
3)
<= 3 mm >= 20 % enine ~ 20 ° C 4)
Mekanik Özellikler
Barlar
3 – 5 mm <= 950 MPa ~ 20 ° C 1)
4)
<= 160 mm 600 – 830 MPa ~ 20 ° C 3)
5)
3 – 5 mm >= 25 % ~ 20 ° C 4)
<= 160 mm >= 25 % boyuna ~ 20 ° C 3)
5)
<= 30 mm >= 370 MPa ~ 50 ° C
<= 30 mm >= 310 MPa ~ 150 ° C
<= 30 mm >= 280 MPa ~ 250 ° C 1)
<= 30 mm >= 25 % enine ~ 20 ° C
<= 30 mm >= 120 J boyuna ~ 20 ° C
<= 30 mm >= 370 MPa ~ 50 ° C
<= 30 mm >= 300 MPa ~ 150 ° C
<= 30 mm >= 265 MPa ~ 250 ° C
<= 30 mm >= 25 % enine ~ 20 ° C
<= 30 mm >= 120 J boyuna ~ 20 ° C
>= 300 MPa ~ 150 ° C
>= 265 MPa ~ 250 ° C
<= 160 mm >= 20 % enine ~ 20 ° C
<= 160 mm >= 60 J enine ~ 20 ° C
Mekanik Özellikler
Barlar
>= 300 MPa ~ 150 ° C
>= 265 MPa ~ 250 ° C
>= 520 MPa ~ 150 ° C 3)
4)
>= 490 MPa ~ 250 ° C 3)
4)
<= 160 mm >= 100 J boyuna ~ 20 ° C 1)