KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
max 0.03 |
max 1 |
max 2 |
max 0.035 |
max 0.015 |
21 – 23 |
2.5 – 3.5 |
4.5 – 6.5 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.1 – 0.22 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
X2CrNiMoN22-5-3 |
S 32205 |
X2CrNiMoN22-5-3 |
Z 3 CND 22-05 Az |
X2CrNiMoN22-5-3 |
X2CrNiMoN22-5-3 |
X2CrNiMoN22-5-3 |
Mekanik Özellikler |
Çözelti ile ısıl işlem görmüş |
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
2)
4) |
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
5) |
<= 75 mm |
>= 150 J |
boyuna |
~ 20 ° C |
|
|
|
|
|
<= 13.5 mm |
>= 460 MPa |
enine |
~ 20 ° C |
|
|
|
|
7) |
3 – 13.5 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
2)
4) |
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
5) |
<= 13.5 mm |
>= 150 J |
boyuna |
~ 20 ° C |
|
|
|
|
|
<= 8 mm |
>= 500 MPa |
enine |
~ 20 ° C |
|
|
|
|
7) |
3 – 8 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 3 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
2)
4) |
<= 3 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
5) |
<= 8 mm |
>= 150 J |
boyuna |
~ 20 ° C |
|
|
|
|
|
|
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 300 MPa |
|
~ 250 ° C |
|
|
|
|
|
Sıcak haddelenmiş levha |
>= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
2)
3) |
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
4) |
>= 10 mm |
>= 60 J |
enine |
~ 20 ° C |
|
|
|
|
|
Sıcak haddelenmiş şerit |
>= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
2)
3) |
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
4) |
>= 10 mm |
>= 60 J |
enine |
~ 20 ° C |
|
|
|
|
|
soğuk haddelenmiş şerit |
>= 3 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 3 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
2)
3) |
<= 3 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
4) |
|
Mekanik Özellikler |
Barlar |
|
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 300 MPa |
|
~ 250 ° C |
|
|
|
|
|
10 – 16 mm |
>= 650 MPa |
|
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
40 – 63 mm |
>= 450 MPa |
|
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
63 – 160 mm |
>= 450 MPa |
|
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
10 – 16 mm |
850 – 1,100 MPa |
|
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
40 – 63 mm |
650 – 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
63 – 160 mm |
650 – 880 MPa |
|
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
10 – 16 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
40 – 63 mm |
>= 15 % |
boyuna |
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
63 – 160 mm |
>= 25 % |
boyuna |
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
40 – 63 mm |
>= 100 J |
boyuna |
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
63 – 160 mm |
>= 100 J |
boyuna |
~ 20 ° C |
|
|
|
|
2)
13)
14)
18) |
Yarı Mamül |
|
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 300 MPa |
|
~ 250 ° C |
|
|
|
|
|
>= 0.05 mm |
900 – 1,100 MPa |
|
|
|
|
|
|
10)
16) |
>= 0.05 mm |
1,100 – 1,350 MPa |
|
|
|
|
|
|
4)
16) |
>= 0.05 mm |
1,400 – 1,700 MPa |
|
|
|
|
|
|
6)
16) |
>= 0.05 mm |
1,800 – 2,100 MPa |
|
|
|
|
|
|
8)
16) |
Kangal |
|
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 300 MPa |
|
~ 250 ° C |
|
|
|
|
|
1 – 3 mm |
<= 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
1)
15) |
5 – 16 mm |
<= 900 MPa |
|
~ 20 ° C |
|
|
|
|
1)
15) |
1 – 3 mm |
>= 20 % |
|
~ 20 ° C |
|
|
|
|
15) |
5 – 16 mm |
>= 25 % |
|
~ 20 ° C |
|
|
|
|
15) |
|
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 300 MPa |
|
~ 250 ° C |
|
|
|
|
|
>= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
2)
3) |
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
4) |
>= 10 mm |
>= 60 J |
enine |
~ 20 ° C |
|
|
|
|
|
Sıcak haddelenmiş şerit |
>= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
2)
3) |
<= 3 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
4) |
>= 10 mm |
>= 60 J |
enine |
~ 20 ° C |
|
|
|
|
|
soğuk haddelenmiş şerit |
>= 3 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 3 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
2)
3) |
<= 3 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
4) |
|
Mekanik Özellikler |
Barlar |
10 – 16 mm |
>= 650 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
40 – 63 mm |
>= 450 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
63 – 160 mm |
>= 450 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
10 – 16 mm |
850 – 1,100 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
40 – 63 mm |
650 – 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
63 – 160 mm |
650 – 880 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
10 – 16 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
40 – 63 mm |
>= 15 % |
boyuna |
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
63 – 160 mm |
>= 25 % |
boyuna |
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
40 – 63 mm |
>= 100 J |
boyuna |
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
63 – 160 mm |
>= 100 J |
boyuna |
~ 20 ° C |
|
|
|
|
2)
5)
6)
9) |
Kangal |
3 – 5 mm |
<= 950 MPa |
|
~ 20 ° C |
|
|
|
|
1)
7) |
<= 160 mm |
650 – 880 MPa |
|
~ 20 ° C |
|
|
|
|
6)
8) |
3 – 5 mm |
>= 25 % |
|
~ 20 ° C |
|
|
|
|
7) |
<= 160 mm |
>= 25 % |
boyuna |
~ 20 ° C |
|
|
|
|
6)
8) |
<= 30 mm |
>= 415 MPa |
|
~ 50 ° C |
|
|
|
|
|
<= 30 mm |
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
<= 30 mm |
>= 295 MPa |
|
~ 250 ° C |
|
|
|
|
2) |
<= 30 mm |
640 – 920 MPa |
|
~ 20 ° C |
|
|
|
|
1) |
<= 30 mm |
>= 22 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 30 mm |
>= 120 J |
boyuna |
~ 20 ° C |
|
|
|
|
|
<= 30 mm |
>= 415 MPa |
|
~ 50 ° C |
|
|
|
|
|
<= 30 mm |
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
<= 30 mm |
>= 295 MPa |
|
~ 250 ° C |
|
|
|
|
|
<= 30 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 30 mm |
>= 120 J |
boyuna |
~ 20 ° C |
|
|
|
|
|
|
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 300 MPa |
|
~ 250 ° C |
|
|
|
|
|
|
>= 570 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 540 MPa |
|
~ 250 ° C |
|
|
|
|
|
<= 350 mm |
>= 25 % |
enine |
~ 20 ° C |
|
|
|
|
|
10 – 350 mm |
>= 100 J |
enine |
~ 20 ° C |
|
|
|
|
|
|
Mekanik Özellikler |
Çekiç Dövme |
|
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 300 MPa |
|
~ 250 ° C |
|
|
|
|
|
<= 350 mm |
>= 20 % |
enine |
~ 20 ° C |
|
|
|
|
|
<= 350 mm |
>= 60 J |
enine |
~ 20 ° C |
|
|
|
|
|
|
Mekanik Özellikler |
Barlar |
5 – 10 mm |
<= 880 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
<= 55 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 900 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 55 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 880 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 55 % |
|
|
|
|
|
|
|
10 – 25 mm |
<= 1,020 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
<= 970 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 50 % |
|
|
|
|
|
|
|
Tel |
5 – 10 mm |
<= 900 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 55 % |
|
|
|
|
|
|
|
10 – 25 mm |
<= 1,020 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
<= 970 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 50 % |
|
|
|
|
|
|
|
Kangal |
5 – 10 mm |
<= 880 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
>= 55 % |
|
|
|
|
|
|
|
5 – 10 mm |
<= 880 MPa |
|
|
|
|
|
|
|
5 – 10 mm |
<= 55 % |
|
|
|
|
|
|
|
<= 0.2 mm |
2,370 – 2,730 MPa |
|
|
|
|
|
|
1)
2)
4) |
0.2 – 0.3 mm |
2,370 – 2,730 MPa |
|
|
|
|
|
|
1)
2)
4) |
0.3 – 0.4 mm |
2,370 – 2,730 MPa |
|
|
|
|
|
|
1)
2)
4) |
0.4 – 0.5 mm |
2,370 – 2,730 MPa |
|
|
|
|
|
|
1)
2)
4) |
0.5 – 0.65 mm |
2,370 – 2,730 MPa |
|
|
|
|
|
|
1)
2)
4) |
0.65 – 0.8 mm |
2,230 – 2,570 MPa |
|
|
|
|
|
|
1)
2)
4) |
0.8 – 1 mm |
2,140 – 2,470 MPa |
|
|
|
|
|
|
1)
2)
4) |
1 – 1.25 mm |
2,090 – 2,410 MPa |
|
|
|
|
|
|
1)
2)
4) |
1.25 – 1.5 mm |
2,090 – 2,410 MPa |
|
|
|
|
|
|
1)
2)
4) |
1.5 – 1.75 mm |
2,000 – 2,300 MPa |
|
|
|
|
|
|
1)
2)
4) |
1.75 – 2 mm |
2,000 – 2,300 MPa |
|
|
|
|
|
|
1)
2)
4) |
2 – 2.5 mm |
1,900 – 2,190 MPa |
|
|
|
|
|
|
1)
2)
4) |
2.5 – 3 mm |
1,860 – 2,140 MPa |
|
|
|
|
|
|
1)
2)
4) |
3.5 – 4.25 mm |
1,450 – 1,670 MPa |
|
|
|
|
|
|
1)
3)
4) |
5 – 6 mm |
1,350 – 1,560 MPa |
|
|
|
|
|
|
1)
3)
4) |
|
>= 335 MPa |
|
~ 150 ° C |
|
|
|
|
|
|
>= 300 MPa |
|
~ 250 ° C |
|
|
|
|
|
|
>= 570 MPa |
|
~ 150 ° C |
|
|
|
|
3)
4) |
|
>= 540 MPa |
|
~ 250 ° C |
|
|
|
|
3)
4) |
<= 160 mm |
>= 100 J |
boyuna |
~ 20 ° C |
|
|
|
|
1) |
|
Mekanik Özellikler |
Çözelti ile ısıl işlem görmüş |
|
>= 22 % |
enine |
|
|
|
|
|
|
|
Mekanik Özellikler |
Boru |
0,2% Verim dayanımı |
boyut |
değer |
numunenin konumu |
|
|
|
|
|
|
<= 30 mm |
>= 450 MPa |
|
|
|
|
|
|
|
Gerilme direnci |
boyut |
değer |
numunenin konumu |
|
|
|
|
|
|
<= 30 mm |
>= 700 MPa |
|
|
|
|
|
|
|
Kırık sonrası uzama (A 5,65) |
boyut |
değer |
numunenin konumu |
|
|
|
|
|
|
<= 30 mm |
>= 22 % |
boyuna |
|
|
|
|
|
|
|
Mekanik Özellikler |
Boru |
Çözelti ile ısıl işlem görmüş |
0,2% Verim dayanımı |
|
değer |
numunenin konumu |
|
|
|
|
|
|
|
>= 450 MPa |
|
|
|
|
|
|
|
1% Verim dayanımı (Rp1,0) |
|
değer |
numunenin konumu |
|
|
|
|
|
|
|
>= 460 MPa |
|
|
|
|
|
|
|
Gerilme direnci |
|
değer |
numunenin konumu |
|
|
|
|
|
|
|
>= 640 MPa |
|
|
|
|
|
|
|
Kırık sonrası uzama (A 5,65) |
|
değer |
numunenin konumu |
|
|
|
|
|
|
|
>= 22 % |
boyuna |
|
|
|
|
|
|
|
Mekanik Özellikler |
Note |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
1)