KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.12 – 0.22 |
max 1 |
max 1.5 |
max 0.04 |
max 0.03 |
15 – 17 |
0.00 |
1.5 – 2.5 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
X17CrNi16-2 |
431 |
X17CrNi16-2 |
Z 15 CN 16-02 |
X17CrNi16-2 |
1Cr17Ni2 |
X17CrNi16-2 |
Mekanik Özellikler |
Barlar |
<= 60 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
18)
21) |
40 – 63 mm |
>= 25 J |
boyuna |
~ 20 ° C |
|
|
|
|
2)
16)
17)
22) |
60 – 160 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
|
>= 565 MPa |
|
~ 100 ° C |
|
|
|
|
18) |
|
>= 525 MPa |
|
~ 150 ° C |
|
|
|
|
18) |
|
>= 505 MPa |
|
~ 200 ° C |
|
|
|
|
18) |
|
>= 490 MPa |
|
~ 250 ° C |
|
|
|
|
18) |
|
>= 470 MPa |
|
~ 300 ° C |
|
|
|
|
18) |
|
>= 430 MPa |
|
~ 350 ° C |
|
|
|
|
18) |
|
>= 375 MPa |
|
~ 400 ° C |
|
|
|
|
18) |
<= 60 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
60 – 160 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
<= 60 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
<= 60 mm |
>= 14 % |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
60 – 160 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
<= 60 mm |
>= 25 J |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
60 – 160 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
Tel |
>= 0.05 mm |
600 – 800 MPa |
|
|
|
|
|
|
10)
20) |
>= 0.05 mm |
800 – 1,000 MPa |
|
|
|
|
|
|
12)
20) |
>= 0.05 mm |
1,000 – 1,250 MPa |
|
|
|
|
|
|
3)
20) |
>= 0.05 mm |
1,200 – 1,450 MPa |
|
|
|
|
|
|
5)
20) |
>= 0.05 mm |
1,600 – 1,900 MPa |
|
|
|
|
|
|
7)
20) |
<= 60 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
Çekilmiş Tel |
1 – 3 mm |
<= 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
1)
19) |
5 – 16 mm |
<= 950 MPa |
|
~ 20 ° C |
|
|
|
|
1)
19) |
1 – 3 mm |
>= 10 % |
|
~ 20 ° C |
|
|
|
|
19) |
5 – 16 mm |
>= 15 % |
|
~ 20 ° C |
|
|
|
|
19) |
|
>= 565 MPa |
|
~ 100 ° C |
|
|
|
|
18) |
|
>= 525 MPa |
|
~ 150 ° C |
|
|
|
|
18) |
|
>= 505 MPa |
|
~ 200 ° C |
|
|
|
|
18) |
|
>= 490 MPa |
|
~ 250 ° C |
|
|
|
|
18) |
|
>= 470 MPa |
|
~ 300 ° C |
|
|
|
|
18) |
|
>= 430 MPa |
|
~ 350 ° C |
|
|
|
|
18) |
|
>= 375 MPa |
|
~ 400 ° C |
|
|
|
|
18) |
<= 60 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
60 – 160 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
<= 60 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
<= 60 mm |
>= 14 % |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
60 – 160 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
<= 60 mm |
>= 25 J |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
60 – 160 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
Bölümler |
|
>= 565 MPa |
|
~ 100 ° C |
|
|
|
|
18) |
|
>= 525 MPa |
|
~ 150 ° C |
|
|
|
|
18) |
|
>= 505 MPa |
|
~ 200 ° C |
|
|
|
|
18) |
|
>= 490 MPa |
|
~ 250 ° C |
|
|
|
|
18) |
|
>= 470 MPa |
|
~ 300 ° C |
|
|
|
|
18) |
|
>= 430 MPa |
|
~ 350 ° C |
|
|
|
|
18) |
|
>= 375 MPa |
|
~ 400 ° C |
|
|
|
|
18) |
<= 60 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
60 – 160 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
<= 60 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
18)
21) |
<= 60 mm |
>= 14 % |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
60 – 160 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
<= 60 mm |
>= 25 J |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
60 – 160 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
17)
21) |
|
Mekanik Özellikler |
Barlar |
<= 10 mm |
<= 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
2)
4)
5)
10) |
16 – 40 mm |
<= 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
10) |
63 – 160 mm |
<= 950 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
10) |
<= 10 mm |
<= 330 HB |
|
~ 20 ° C |
|
|
|
|
2)
3)
4)
5)
10) |
16 – 40 mm |
<= 310 HB |
|
~ 20 ° C |
|
|
|
|
2)
3)
5)
10) |
63 – 160 mm |
<= 295 HB |
|
~ 20 ° C |
|
|
|
|
2)
3)
5)
10) |
10 – 16 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
10) |
<= 60 mm |
>= 600 MPa |
|
~ 20 ° C |
|
|
|
|
6)
9) |
40 – 63 mm |
>= 650 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
10) |
60 – 160 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
10 – 16 mm |
850 – 1,100 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
10) |
<= 60 mm |
800 – 950 MPa |
|
~ 20 ° C |
|
|
|
|
6)
9) |
40 – 63 mm |
800 – 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
2)
5)
6)
10) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
10 – 16 mm |
>= 7 % |
boyuna |
~ 20 ° C |
|
|
|
|
2)
5)
6)
10) |
<= 60 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
7)
9) |
40 – 63 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
2)
5)
6)
10) |
60 – 160 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
<= 60 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
7)
9) |
40 – 63 mm |
>= 25 J |
boyuna |
~ 20 ° C |
|
|
|
|
2)
5)
6)
10) |
60 – 160 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
<= 60 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
Çekilmiş Tel |
1 – 3 mm |
<= 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
1)
8) |
5 – 16 mm |
<= 950 MPa |
|
~ 20 ° C |
|
|
|
|
1)
8) |
3 – 5 mm |
>= 10 % |
|
~ 20 ° C |
|
|
|
|
8) |
<= 60 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
60 – 160 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
<= 60 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
<= 60 mm |
>= 14 % |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
60 – 160 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
<= 60 mm |
>= 25 J |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
60 – 160 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
Bölümler |
<= 60 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
60 – 160 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
<= 60 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
7)
9) |
<= 60 mm |
>= 14 % |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
60 – 160 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
<= 60 mm |
>= 25 J |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
60 – 160 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
6)
9) |
|
Mekanik Özellikler |
Çekiç Dövme |
<= 250 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
2) |
<= 250 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
2) |
<= 250 mm |
>= 10 % |
boyuna |
~ 20 ° C |
|
|
|
|
2) |
<= 250 mm |
>= 8 % |
enine |
~ 20 ° C |
|
|
|
|
2) |
<= 250 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
1) |
<= 250 mm |
>= 15 J |
enine |
~ 20 ° C |
|
|
|
|
1) |
|
Mekanik Özellikler |
Barlar |
|
>= 565 MPa |
|
~ 100 ° C |
|
|
|
|
3) |
|
>= 525 MPa |
|
~ 150 ° C |
|
|
|
|
3) |
|
>= 505 MPa |
|
~ 200 ° C |
|
|
|
|
3) |
|
>= 490 MPa |
|
~ 250 ° C |
|
|
|
|
3) |
|
>= 470 MPa |
|
~ 300 ° C |
|
|
|
|
3) |
|
>= 430 MPa |
|
~ 350 ° C |
|
|
|
|
3) |
|
>= 375 MPa |
|
~ 400 ° C |
|
|
|
|
3) |
<= 60 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
3) |
60 – 160 mm |
>= 700 MPa |
|
~ 20 ° C |
|
|
|
|
3) |
<= 60 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
3) |
60 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
3) |
<= 60 mm |
>= 14 % |
boyuna |
~ 20 ° C |
|
|
|
|
2) |
60 – 160 mm |
>= 12 % |
boyuna |
~ 20 ° C |
|
|
|
|
2) |
<= 60 mm |
>= 25 J |
boyuna |
~ 20 ° C |
|
|
|
|
2) |
60 – 160 mm |
>= 20 J |
boyuna |
~ 20 ° C |
|
|
|
|
2) |
tavlı and cold reÇekilmiş |
Gerilme direnci |
boyut |
değer |
numunenin konumu |
sıcaklığı |
|
|
|
|
|
<= 35 mm |
<= 1,100 MPa |
|
~ 20 ° C |
|
|
|
|
|
Sertlik [HBW] |
boyut |
değer |
numunenin konumu |
sıcaklığı |
|
|
|
|
|
<= 35 mm |
<= 355 HBW |
|
~ 20 ° C |
|
|
|
|
1) |
|