KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.35 – 0.4 |
max 0.4 |
1.2 – 1.5 |
max 0.06 |
0.24 – 0.33 |
0.00 |
0.00 |
0.00 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
38SMn28 |
38SMn28 |
38SMn28 |
38SMn28 |
38SMn28 |
38SMn28 |
38SMn28 |
Mekanik Özellikler |
haddelenmiş ve parlaklaştırılmış |
40 – 63 mm |
560 – 730 MPa |
|
|
|
|
|
|
|
40 – 63 mm |
166 – 216 HBW |
|
|
|
|
|
|
4) |
40 – 63 mm |
>= 400 MPa |
|
|
|
|
|
|
2) |
40 – 63 mm |
700 – 850 MPa |
|
|
|
|
|
|
2) |
40 – 63 mm |
>= 16 % |
|
|
|
|
|
|
2) |
40 – 63 mm |
>= 400 MPa |
|
|
|
|
|
|
2) |
40 – 63 mm |
700 – 850 MPa |
|
|
|
|
|
|
2) |
40 – 63 mm |
>= 16 % |
|
|
|
|
|
|
2) |
10 – 16 mm |
>= 500 MPa |
|
|
|
|
|
|
3) |
40 – 63 mm |
>= 400 MPa |
|
|
|
|
|
|
3) |
10 – 16 mm |
660 – 930 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
600 – 840 MPa |
|
|
|
|
|
|
1) |
10 – 16 mm |
>= 6 % |
|
|
|
|
|
|
|
40 – 63 mm |
>= 7 % |
|
|
|
|
|
|
|
10 – 16 mm |
>= 545 MPa |
|
|
|
|
|
|
2) |
40 – 63 mm |
>= 490 MPa |
|
|
|
|
|
|
2) |
10 – 16 mm |
775 – 925 MPa |
|
|
|
|
|
|
2) |
40 – 63 mm |
700 – 900 MPa |
|
|
|
|
|
|
2) |
10 – 16 mm |
>= 10 % |
|
|
|
|
|
|
2) |
40 – 63 mm |
>= 13 % |
|
|
|
|
|
|
2) |
63 – 100 mm |
>= 14 % |
|
|
|
|
|
|
2) |
|