KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.52 – 0.60 |
<=0.40 |
0.60 – 0.90 |
<=0.035 |
<=0.035 |
<=0.40 |
<=0.10 |
<=0.40 |
|
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
|
|
|
|
|
|
|
|
|
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
C55E |
1055 |
CK 55 |
XC 55 H1 |
C55 |
55 |
C55E |
Mekanik Özellikler |
Yüzey Sertlik [HRC] |
~ 2 mm |
55 – 64 HRC |
|
|
|
|
|
|
4) |
~ 4 mm |
37 – 62 HRC |
|
|
|
|
|
|
4) |
~ 6 mm |
32 – 57 HRC |
|
|
|
|
|
|
4) |
~ 8 mm |
30 – 45 HRC |
|
|
|
|
|
|
4) |
~ 10 mm |
28 – 36 HRC |
|
|
|
|
|
|
4) |
~ 13 mm |
26 – 34 HRC |
|
|
|
|
|
|
4) |
~ 20 mm |
24 – 32 HRC |
|
|
|
|
|
|
4) |
~ 30 mm |
20 – 29 HRC |
|
|
|
|
|
|
4) |
~ 5 mm |
42 – 60 HRC |
|
|
|
|
|
|
5) |
~ 5 mm |
33 – 51 HRC |
|
|
|
|
|
|
6) |
Suverilmiş ve menevişlenmiş |
16 – 40 mm |
>= 490 MPa |
|
~ 20 ° C |
|
|
|
|
7) |
16 – 40 mm |
750 – 900 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 14 % |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 35 % |
|
~ 20 ° C |
|
|
|
|
|
16 – 100 mm |
>= 330 MPa |
|
~ 20 ° C |
|
|
|
|
7) |
16 – 100 mm |
>= 640 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 100 mm |
>= 12 % |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 490 MPa |
|
~ 20 ° C |
|
|
|
|
7) |
8 – 20 mm |
750 – 900 MPa |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 14 % |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 35 % |
|
~ 20 ° C |
|
|
|
|
|
70 – 160 mm |
>= 360 MPa |
|
|
|
|
|
|
|
70 – 160 mm |
>= 630 MPa |
|
|
|
|
|
|
|
70 – 160 mm |
>= 17 % |
boyuna |
|
|
|
|
|
|
160 – 330 mm |
>= 16 % |
boyuna |
|
|
|
|
|
|
100 – 250 mm |
>= 300 MPa |
|
|
|
|
|
|
|
500 – 1,000 mm |
>= 250 MPa |
|
|
|
|
|
|
|
100 – 250 mm |
>= 620 MPa |
|
|
|
|
|
|
|
500 – 1,000 mm |
>= 590 MPa |
|
|
|
|
|
|
|
100 – 250 mm |
>= 12 % |
boyuna |
|
|
|
|
|
|
250 – 500 mm |
>= 12 % |
boyuna |
|
|
|
|
|
|
500 – 1,000 mm |
>= 11 % |
boyuna |
|
|
|
|
|
|
100 – 250 mm |
>= 300 MPa |
|
|
|
|
|
|
|
500 – 1,000 mm |
>= 250 MPa |
|
|
|
|
|
|
|
100 – 250 mm |
>= 620 MPa |
|
|
|
|
|
|
|
500 – 1,000 mm |
>= 590 MPa |
|
|
|
|
|
|
|
100 – 250 mm |
>= 12 % |
boyuna |
|
|
|
|
|
|
250 – 500 mm |
>= 12 % |
boyuna |
|
|
|
|
|
|
500 – 1,000 mm |
>= 11 % |
boyuna |
|
|
|
|
|
|
500 – 1,000 mm |
>= 8 % |
enine |
|
|
|
|
|
|
|