KİMYASAL BİLEŞİM
| C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
| 0.37 – 0.44 |
<=0.40 |
0.50 – 0.80 |
<=0.045 |
<=0.045 |
<=0.40 |
<=0.10 |
<=0.40 |
|
| Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
|
|
|
|
|
|
|
|
|
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
| C40 |
1040 |
C40 |
AF 60 |
C40 |
C40 |
C40 |
| Mekanik Özellikler |
| normalleştirilmiş |
| 16 – 40 mm |
>= 18 % |
|
~ 20 ° C |
|
|
|
|
|
| 16 – 40 mm |
>= 40 % |
|
~ 20 ° C |
|
|
|
|
|
| 16 – 100 mm |
>= 290 MPa |
|
~ 20 ° C |
|
|
|
|
4) |
| 16 – 100 mm |
>= 550 MPa |
|
~ 20 ° C |
|
|
|
|
|
| 16 – 100 mm |
>= 17 % |
|
~ 20 ° C |
|
|
|
|
|
| 8 – 20 mm |
>= 400 MPa |
|
~ 20 ° C |
|
|
|
|
4) |
| 8 – 20 mm |
630 – 780 MPa |
|
~ 20 ° C |
|
|
|
|
|
| 8 – 20 mm |
>= 18 % |
|
~ 20 ° C |
|
|
|
|
|
| 8 – 20 mm |
>= 40 % |
|
~ 20 ° C |
|
|
|
|
|
| 100 – 250 mm |
>= 260 MPa |
|
|
|
|
|
|
|
| 100 – 250 mm |
>= 530 MPa |
|
|
|
|
|
|
|
| 100 – 250 mm |
>= 17 % |
boyuna |
|
|
|
|
|
|
| 100 – 250 mm |
>= 260 MPa |
|
|
|
|
|
|
|
| 100 – 250 mm |
>= 530 MPa |
|
|
|
|
|
|
|
| 100 – 250 mm |
>= 17 % |
boyuna |
|
|
|
|
|
|
|
| Mekanik Özellikler |
| haddelenmiş ve parlaklaştırılmış |
| 40 – 63 mm |
550 – 710 MPa |
|
|
|
|
|
|
|
| 40 – 63 mm |
163 – 211 HBW |
|
|
|
|
|
|
3) |
| 10 – 16 mm |
>= 460 MPa |
|
|
|
|
|
|
1) |
| 40 – 63 mm |
>= 330 MPa |
|
|
|
|
|
|
1) |
| 10 – 16 mm |
650 – 980 MPa |
|
|
|
|
|
|
2) |
| 40 – 63 mm |
590 – 840 MPa |
|
|
|
|
|
|
2) |
| 10 – 16 mm |
>= 7 % |
|
|
|
|
|
|
|
| 40 – 63 mm |
>= 9 % |
|
|
|
|
|
|
|
| 63 – 100 mm |
>= 9 % |
|
|
|
|
|
|
|
|