KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.37 – 0.44 |
max 0.4 |
0.5 – 0.8 |
max 0.03 |
0.02 – 0.04 |
max 0.4 |
max 0.1 |
max 0.4 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
C40R |
1040 |
C40R |
XC 42 H 1 u |
C40 |
C40R |
C40R |
Mekanik Özellikler |
normalleştirilmiş |
~ 4 mm |
38 – 57 HRC |
|
|
|
|
|
|
5) |
~ 4 mm |
27 – 46 HRC |
|
|
|
|
|
|
6) |
Suverilmiş ve menevişlenmiş |
16 – 40 mm |
>= 400 MPa |
|
~ 20 ° C |
|
|
|
|
8) |
16 – 40 mm |
630 – 780 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 18 % |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 40 % |
|
~ 20 ° C |
|
|
|
|
|
40 – 100 mm |
>= 30 J |
boyuna |
~ 20 ° C |
|
|
|
|
1) |
kesmeye hazır halde |
16 – 100 mm |
>= 290 MPa |
|
~ 20 ° C |
|
|
|
|
8) |
16 – 100 mm |
>= 550 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 100 mm |
>= 17 % |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 400 MPa |
|
~ 20 ° C |
|
|
|
|
8) |
8 – 20 mm |
630 – 780 MPa |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 18 % |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 40 % |
|
~ 20 ° C |
|
|
|
|
|
20 – 60 mm |
>= 30 J |
boyuna |
~ 20 ° C |
|
|
|
|
1) |
|
Mekanik Özellikler |
haddelenmiş ve parlaklaştırılmış |
40 – 63 mm |
550 – 710 MPa |
|
|
|
|
|
|
|
40 – 63 mm |
163 – 211 HBW |
|
|
|
|
|
|
|
40 – 63 mm |
>= 350 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
600 – 750 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 19 % |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 350 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
600 – 750 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 19 % |
|
|
|
|
|
|
1) |
10 – 16 mm |
>= 460 MPa |
|
|
|
|
|
|
2) |
40 – 63 mm |
>= 330 MPa |
|
|
|
|
|
|
2) |
10 – 16 mm |
650 – 980 MPa |
|
|
|
|
|
|
3) |
40 – 63 mm |
590 – 840 MPa |
|
|
|
|
|
|
3) |
10 – 16 mm |
>= 7 % |
|
|
|
|
|
|
|
40 – 63 mm |
>= 9 % |
|
|
|
|
|
|
|
10 – 16 mm |
>= 525 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 435 MPa |
|
|
|
|
|
|
1) |
10 – 16 mm |
750 – 950 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
620 – 820 MPa |
|
|
|
|
|
|
1) |
10 – 16 mm |
>= 8 % |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 10 % |
|
|
|
|
|
|
1) |
63 – 100 mm |
>= 11 % |
|
|
|
|
|
|
1) |
|