KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.46 – 0.54 |
max 0.4 |
0.5 – 0.8 |
max 0.025 |
max 0.035 |
0.9 – 1.2 |
0.15 – 0.3 |
0.00 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
50CrMo4 |
4150 |
50CrMo4 |
50CrMo4 |
50CrMo4 |
ZG50CrMo |
50CrMo4 |
Mekanik Özellikler |
Yüzey Sertlik [HRC] |
16 – 40 mm |
>= 780 MPa |
|
~ 20 ° C |
|
|
|
|
9) |
100 – 160 mm |
>= 650 MPa |
|
~ 20 ° C |
|
|
|
|
9) |
16 – 40 mm |
1,000 – 1,200 MPa |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
850 – 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 10 % |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
>= 13 % |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 45 % |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
>= 50 % |
|
~ 20 ° C |
|
|
|
|
|
40 – 100 mm |
>= 30 J |
|
~ 20 ° C |
|
|
|
|
1) |
160 – 250 mm |
>= 30 J |
|
~ 20 ° C |
|
|
|
|
1) |
kesmeye hazır halde |
8 – 20 mm |
>= 780 MPa |
|
~ 20 ° C |
|
|
|
|
9) |
60 – 100 mm |
>= 650 MPa |
|
~ 20 ° C |
|
|
|
|
9) |
8 – 20 mm |
1,000 – 1,200 MPa |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
850 – 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 10 % |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
>= 13 % |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 45 % |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
>= 50 % |
|
~ 20 ° C |
|
|
|
|
|
20 – 60 mm |
>= 30 J |
|
~ 20 ° C |
|
|
|
|
1) |
100 – 160 mm |
>= 30 J |
|
~ 20 ° C |
|
|
|
|
1) |
|
Mekanik Özellikler |
Çekiç Dövme |
160 – 330 mm |
>= 540 MPa |
|
|
|
|
|
|
|
160 – 330 mm |
>= 750 MPa |
|
|
|
|
|
|
|
<= 160 mm |
>= 9 % |
enine |
|
|
|
|
|
|
160 – 330 mm |
>= 10 % |
enine |
|
|
|
|
|
|
330 – 500 mm |
>= 11 % |
enine |
|
|
|
|
|
|
<= 160 mm |
>= 14 J |
enine |
|
|
|
|
|
|
160 – 330 mm |
>= 12 J |
enine |
|
|
|
|
|
|
330 – 500 mm |
>= 10 J |
enine |
|
|
|
|
|
|
|
Mekanik Özellikler |
Barlar |
16 – 40 mm |
>= 780 MPa |
|
~ 20 ° C |
|
|
|
|
3) |
100 – 160 mm |
>= 650 MPa |
|
~ 20 ° C |
|
|
|
|
3) |
16 – 40 mm |
1,000 – 1,200 MPa |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
850 – 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 10 % |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
>= 13 % |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 45 % |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
>= 50 % |
|
~ 20 ° C |
|
|
|
|
|
40 – 100 mm |
>= 30 J |
boyuna |
~ 20 ° C |
|
|
|
|
1) |
160 – 250 mm |
>= 30 J |
boyuna |
~ 20 ° C |
|
|
|
|
1) |
Yassı Ürünler |
8 – 20 mm |
>= 780 MPa |
|
~ 20 ° C |
|
|
|
|
2)
3) |
60 – 100 mm |
>= 650 MPa |
|
~ 20 ° C |
|
|
|
|
2)
3) |
8 – 20 mm |
1,000 – 1,200 MPa |
|
~ 20 ° C |
|
|
|
|
2) |
60 – 100 mm |
850 – 1,000 MPa |
|
~ 20 ° C |
|
|
|
|
2) |
8 – 20 mm |
>= 10 % |
|
~ 20 ° C |
|
|
|
|
2) |
60 – 100 mm |
>= 13 % |
|
~ 20 ° C |
|
|
|
|
2) |
8 – 20 mm |
>= 45 % |
|
~ 20 ° C |
|
|
|
|
2) |
60 – 100 mm |
>= 50 % |
|
~ 20 ° C |
|
|
|
|
2) |
20 – 60 mm |
>= 30 J |
boyuna |
~ 20 ° C |
|
|
|
|
1) |
100 – 160 mm |
>= 30 J |
boyuna |
~ 20 ° C |
|
|
|
|
1) |
|
Mekanik Özellikler |
Dövme Parçaları |
<= 250 mm |
>= 554 MPa |
|
~ 100 ° C |
|
|
|
|
1) |
<= 250 mm |
>= 490 MPa |
|
~ 250 ° C |
|
|
|
|
1) |
<= 250 mm |
>= 412 MPa |
|
~ 350 ° C |
|
|
|
|
1) |
250 – 500 mm |
>= 540 MPa |
|
~ 20 ° C |
|
|
|
|
1) |
250 – 500 mm |
>= 481 MPa |
|
~ 200 ° C |
|
|
|
|
1) |
250 – 500 mm |
>= 431 MPa |
|
~ 300 ° C |
|
|
|
|
1) |
250 – 500 mm |
>= 353 MPa |
|
~ 400 ° C |
|
|
|
|
1) |
500 – 750 mm |
>= 461 MPa |
|
~ 100 ° C |
|
|
|
|
1) |
500 – 750 mm |
>= 402 MPa |
|
~ 250 ° C |
|
|
|
|
1) |
500 – 750 mm |
>= 333 MPa |
|
~ 350 ° C |
|
|
|
|
1) |
250 – 500 mm |
740 – 890 MPa |
|
~ 20 ° C |
|
|
|
|
|
<= 250 mm |
>= 9 % |
enine |
~ 20 ° C |
|
|
|
|
3) |
250 – 500 mm |
>= 14 % |
boyuna |
~ 20 ° C |
|
|
|
|
4) |
250 – 500 mm |
>= 12 % |
yüzeysel |
~ 20 ° C |
|
|
|
|
2) |
500 – 750 mm |
>= 11 % |
enine |
~ 20 ° C |
|
|
|
|
3) |
<= 250 mm |
>= 14 J |
enine |
~ 20 ° C |
|
|
|
|
3) |
250 – 500 mm |
>= 31 J |
boyuna |
~ 20 ° C |
|
|
|
|
4) |
250 – 500 mm |
>= 24 J |
yüzeysel |
~ 20 ° C |
|
|
|
|
2) |
500 – 750 mm |
>= 14 J |
enine |
~ 20 ° C |
|
|
|
|
3) |
500 – 750 mm |
>= 24 J |
yüzeysel |
~ 20 ° C |
|
|
|
|
2) |
|