KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.38 – 0.45 |
max 0.4 |
0.6 – 0.9 |
max 0.025 |
0.02 – 0.04 |
0.9 – 1.2 |
0.00 |
0.00 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
41CrS4 |
5140 |
41CrS4 |
42 C 4 u |
41CrS4 |
41CrS4 |
41CrS4 |
Mekanik Özellikler |
Yüzey Sertlik [HRC] |
16 – 40 mm |
>= 660 MPa |
|
~ 20 ° C |
|
|
|
|
9) |
16 – 40 mm |
900 – 1,100 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 12 % |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 35 % |
|
~ 20 ° C |
|
|
|
|
|
40 – 100 mm |
>= 35 J |
|
~ 20 ° C |
|
|
|
|
1) |
kesmeye hazır halde |
8 – 20 mm |
>= 660 MPa |
|
~ 20 ° C |
|
|
|
|
9) |
8 – 20 mm |
900 – 1,100 MPa |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 12 % |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 35 % |
|
~ 20 ° C |
|
|
|
|
|
20 – 60 mm |
>= 35 J |
|
~ 20 ° C |
|
|
|
|
1) |
|
Mekanik Özellikler |
Çekirdek sertleşme testi |
~ 3 mm |
52 – 61 HRC |
|
|
|
|
|
|
|
~ 7 mm |
47 – 59 HRC |
|
|
|
|
|
|
|
~ 11 mm |
40 – 56 HRC |
|
|
|
|
|
|
|
~ 15 mm |
35 – 52 HRC |
|
|
|
|
|
|
|
~ 25 mm |
27 – 42 HRC |
|
|
|
|
|
|
|
~ 35 mm |
23 – 38 HRC |
|
|
|
|
|
|
|
~ 45 mm |
21 – 36 HRC |
|
|
|
|
|
|
|
~ 3 mm |
55 – 61 HRC |
|
|
|
|
|
|
|
~ 7 mm |
51 – 59 HRC |
|
|
|
|
|
|
|
~ 11 mm |
43 – 56 HRC |
|
|
|
|
|
|
|
~ 15 mm |
39 – 52 HRC |
|
|
|
|
|
|
|
~ 25 mm |
31 – 42 HRC |
|
|
|
|
|
|
|
~ 35 mm |
27 – 38 HRC |
|
|
|
|
|
|
|
~ 45 mm |
25 – 36 HRC |
|
|
|
|
|
|
|
~ 3 mm |
52 – 58 HRC |
|
|
|
|
|
|
|
~ 7 mm |
47 – 55 HRC |
|
|
|
|
|
|
|
~ 11 mm |
40 – 50 HRC |
|
|
|
|
|
|
|
~ 15 mm |
35 – 45 HRC |
|
|
|
|
|
|
|
~ 25 mm |
27 – 37 HRC |
|
|
|
|
|
|
|
~ 35 mm |
23 – 32 HRC |
|
|
|
|
|
|
|
~ 45 mm |
21 – 30 HRC |
|
|
|
|
|
|
|
5 – 40 mm |
<= 600 MPa |
|
|
|
|
|
|
|
5 – 40 mm |
>= 60 % |
|
|
|
|
|
|
|
5 – 40 mm |
<= 640 MPa |
|
|
|
|
|
|
|
5 – 40 mm |
>= 58 % |
|
|
|
|
|
|
|
5 – 40 mm |
<= 600 MPa |
|
|
|
|
|
|
|
5 – 40 mm |
>= 60 % |
|
|
|
|
|
|
|
5 – 40 mm |
<= 640 MPa |
|
|
|
|
|
|
|
5 – 40 mm |
>= 58 % |
|
|
|
|
|
|
|
Kangal |
40 – 63 mm |
<= 241 HBW |
|
|
|
|
|
|
|
40 – 63 mm |
>= 560 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
800 – 950 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 14 % |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 560 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
800 – 950 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 14 % |
|
|
|
|
|
|
1) |
10 – 16 mm |
<= 285 HBW |
|
|
|
|
|
|
|
40 – 63 mm |
<= 270 HBW |
|
|
|
|
|
|
|
10 – 16 mm |
>= 750 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 570 MPa |
|
|
|
|
|
|
1) |
10 – 16 mm |
1,000 – 1,200 MPa |
|
|
|
|
|
|
1)
2) |
40 – 63 mm |
800 – 1,000 MPa |
|
|
|
|
|
|
1)
2) |
10 – 16 mm |
>= 8 % |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 10 % |
|
|
|
|
|
|
1) |
63 – 100 mm |
>= 11 % |
|
|
|
|
|
|
1) |
|