KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.35 – 0.43 |
max 0.4 |
0.5 – 0.8 |
max 0.025 |
max 0.035 |
0.6 – 1 |
0.15 – 0.25 |
0.7 – 1 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
39NiCrMo3 |
39NiCrMo3 |
39NiCrMo3 |
39NiCrMo3 |
39NiCrMo3 |
39NiCrMo3 |
39NiCrMo3 |
Mekanik Özellikler |
hafif tavlı |
16 – 40 mm |
930 – 1,130 MPa |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
830 – 980 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 11 % |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
>= 12 % |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 40 % |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
>= 50 % |
|
~ 20 ° C |
|
|
|
|
|
40 – 100 mm |
>= 40 J |
|
~ 20 ° C |
|
|
|
|
1) |
160 – 250 mm |
>= 40 J |
|
~ 20 ° C |
|
|
|
|
1) |
kesmeye hazır halde |
8 – 20 mm |
>= 735 MPa |
|
~ 20 ° C |
|
|
|
|
8) |
60 – 100 mm |
>= 635 MPa |
|
~ 20 ° C |
|
|
|
|
8) |
8 – 20 mm |
930 – 1,130 MPa |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
830 – 980 MPa |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 11 % |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
>= 12 % |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 40 % |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
>= 50 % |
|
~ 20 ° C |
|
|
|
|
|
20 – 60 mm |
>= 40 J |
|
~ 20 ° C |
|
|
|
|
1) |
100 – 160 mm |
>= 40 J |
|
~ 20 ° C |
|
|
|
|
1) |
|
Mekanik Özellikler |
tavlı ve parlatılmış |
40 – 63 mm |
<= 240 HBW |
|
|
|
|
|
|
|
40 – 63 mm |
>= 735 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
880 – 1,080 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 12 % |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 735 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
880 – 1,080 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 12 % |
|
|
|
|
|
|
1) |
10 – 16 mm |
<= 290 HBW |
|
|
|
|
|
|
|
40 – 63 mm |
<= 280 HBW |
|
|
|
|
|
|
|
10 – 16 mm |
>= 700 MPa |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 625 MPa |
|
|
|
|
|
|
1) |
10 – 16 mm |
930 – 1,130 MPa |
|
|
|
|
|
|
1)
2) |
40 – 63 mm |
880 – 1,080 MPa |
|
|
|
|
|
|
1)
2) |
10 – 16 mm |
>= 8 % |
|
|
|
|
|
|
1) |
40 – 63 mm |
>= 10 % |
|
|
|
|
|
|
1) |
63 – 100 mm |
>= 10 % |
|
|
|
|
|
|
1) |
|