Ürün Materyel No
1.7034
Ürün Adı
37Cr4

KİMYASAL BİLEŞİM

C Si Mn P S Cr Mo Ni V
0.34 – 0.41 max 0.4 0.6 – 0.9 max 0.025 max 0.035 0.9 – 1.2 0.00 0.00 0.00
Al Cu Pb N Ti Br Sc Bh Sn
0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00

STANDARTLARIN KARŞILAŞTIRILMASI

Avrupa
EURO
Almanya
DIN
Amerika
AISI-SAE
Fransa
AFNOR
İtalya
UNI
Çin
GB
Türkiye
TSE
37Cr4 5135 37Cr4 38 C 4 38 Cr 4 KB 35Cr 37Cr4
Mekanik Özellikler
Yüzey Sertlik [HRC]
16 – 40 mm >= 630 MPa ~ 20 ° C 8)
16 – 40 mm 850 – 1,000 MPa ~ 20 ° C
16 – 40 mm >= 13 % ~ 20 ° C
16 – 40 mm >= 40 % ~ 20 ° C
40 – 100 mm >= 35 J ~ 20 ° C 1)
kesmeye hazır halde
8 – 20 mm >= 630 MPa ~ 20 ° C 8)
8 – 20 mm 850 – 1,000 MPa ~ 20 ° C
8 – 20 mm >= 13 % ~ 20 ° C
8 – 20 mm >= 40 % ~ 20 ° C
20 – 60 mm >= 35 J ~ 20 ° C 1)
Mekanik Özellikler
Çekiç Dövme
~ 3 mm 50 – 59 HRC
~ 7 mm 44 – 57 HRC
~ 11 mm 36 – 52 HRC
~ 15 mm 31 – 48 HRC
~ 25 mm 24 – 39 HRC
~ 35 mm 20 – 36 HRC
~ 45 mm <= 34 HRC
~ 3 mm 53 – 59 HRC
~ 7 mm 48 – 57 HRC
~ 11 mm 41 – 52 HRC
~ 15 mm 37 – 48 HRC
~ 25 mm 29 – 39 HRC
~ 35 mm 25 – 36 HRC
~ 45 mm 23 – 34 HRC
~ 3 mm 50 – 56 HRC
~ 7 mm 44 – 53 HRC
~ 11 mm 36 – 47 HRC
~ 15 mm 31 – 42 HRC
~ 25 mm 24 – 34 HRC
~ 35 mm 20 – 31 HRC
~ 45 mm <= 29 HRC
5 – 40 mm <= 570 MPa
5 – 40 mm >= 62 %
5 – 40 mm <= 610 MPa
5 – 40 mm >= 60 %
5 – 40 mm <= 570 MPa
5 – 40 mm >= 62 %
5 – 40 mm <= 610 MPa
5 – 40 mm >= 60 %
Kangal
tavlı to elde küresel parçacıklar karbürler + soyulmuş ocak
Gerilme direnci
boyut değer
5 – 40 mm <= 590 MPa
alanın azaltılması
boyut değer
5 – 40 mm >= 60 %
tavlı küresel parçacıklar karbür elde etmek üzere
Gerilme direnci
boyut değer
5 – 40 mm <= 590 MPa
alanın azaltılması
boyut değer
5 – 40 mm >= 60 %