KİMYASAL BİLEŞİM
| C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
| 0.3 – 0.7 |
max 0.4 |
0.6 – 0.9 |
max 0.025 |
0.02 – 0.04 |
0.9 – 1.2 |
0.00 |
0.00 |
0.00 |
| Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
| 0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
| 34CrS4 |
5132 |
34CrS4 |
32 C 4 u |
34CrS4 |
34CrS4 |
34CrS4 |
| Mekanik Özellikler |
| hafif tavlı |
| 16 – 40 mm |
800 – 950 MPa |
|
~ 20 ° C |
|
|
|
|
|
| 16 – 40 mm |
>= 14 % |
|
~ 20 ° C |
|
|
|
|
|
| 16 – 40 mm |
>= 40 % |
|
~ 20 ° C |
|
|
|
|
|
| 40 – 100 mm |
>= 40 J |
|
~ 20 ° C |
|
|
|
|
1) |
| kesmeye hazır halde |
| 8 – 20 mm |
>= 590 MPa |
|
~ 20 ° C |
|
|
|
|
7) |
| 8 – 20 mm |
800 – 950 MPa |
|
~ 20 ° C |
|
|
|
|
|
| 8 – 20 mm |
>= 14 % |
|
~ 20 ° C |
|
|
|
|
|
| 8 – 20 mm |
>= 40 % |
|
~ 20 ° C |
|
|
|
|
|
| 20 – 60 mm |
>= 40 J |
|
~ 20 ° C |
|
|
|
|
1) |
|
| Mekanik Özellikler |
| tavlı ve parlatılmış |
| 40 – 63 mm |
<= 223 HBW |
|
|
|
|
|
|
|
| 40 – 63 mm |
>= 460 MPa |
|
|
|
|
|
|
2) |
| 40 – 63 mm |
700 – 850 MPa |
|
|
|
|
|
|
2) |
| 40 – 63 mm |
>= 15 % |
|
|
|
|
|
|
2) |
| 40 – 63 mm |
>= 460 MPa |
|
|
|
|
|
|
2) |
| 40 – 63 mm |
700 – 850 MPa |
|
|
|
|
|
|
2) |
| 40 – 63 mm |
>= 15 % |
|
|
|
|
|
|
2) |
| 10 – 16 mm |
<= 275 HBW |
|
|
|
|
|
|
|
| 40 – 63 mm |
<= 265 HBW |
|
|
|
|
|
|
|
| 10 – 16 mm |
>= 700 MPa |
|
|
|
|
|
|
2) |
| 40 – 63 mm |
>= 510 MPa |
|
|
|
|
|
|
2) |
| 10 – 16 mm |
900 – 1,100 MPa |
|
|
|
|
|
|
1)
2) |
| 40 – 63 mm |
700 – 900 MPa |
|
|
|
|
|
|
1)
2) |
| 10 – 16 mm |
>= 9 % |
|
|
|
|
|
|
2) |
| 40 – 63 mm |
>= 10 % |
|
|
|
|
|
|
2) |
| 63 – 100 mm |
>= 11 % |
|
|
|
|
|
|
2) |
|