KİMYASAL BİLEŞİM
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
V |
0.26 – 0.33 |
max 0.4 |
0.5 – 0.8 |
max 0.025 |
max 0.025 |
1.2 – 1.5 |
0.3 – 0.6 |
3.3 – 4.3 |
0.00 |
Al |
Cu |
Pb |
N |
Ti |
Br |
Sc |
Bh |
Sn |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
0.00 |
STANDARTLARIN KARŞILAŞTIRILMASI
Avrupa
EURO |
Almanya
DIN |
Amerika
AISI-SAE |
Fransa
AFNOR |
İtalya
UNI |
Çin
GB |
Türkiye
TSE |
30NiCrMo16-6 |
30NiCrMo16-6 |
30NiCrMo16-6 |
35 NCD 16 |
30NiCrMo16-6 |
30NiCrMo16-6 |
30NiCrMo16-6 |
Mekanik Özellikler |
hafif tavlı |
16 – 40 mm |
1,080 – 1,230 MPa |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 10 % |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
>= 11 % |
|
~ 20 ° C |
|
|
|
|
|
16 – 40 mm |
>= 45 % |
|
~ 20 ° C |
|
|
|
|
|
100 – 160 mm |
>= 50 % |
|
~ 20 ° C |
|
|
|
|
|
40 – 100 mm |
>= 35 J |
|
~ 20 ° C |
|
|
|
|
1) |
160 – 250 mm |
>= 35 J |
|
~ 20 ° C |
|
|
|
|
1) |
kesmeye hazır halde |
8 – 20 mm |
>= 880 MPa |
|
~ 20 ° C |
|
|
|
|
8) |
60 – 100 mm |
>= 790 MPa |
|
~ 20 ° C |
|
|
|
|
8) |
8 – 20 mm |
1,080 – 1,230 MPa |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
900 – 1,050 MPa |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 10 % |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
>= 11 % |
|
~ 20 ° C |
|
|
|
|
|
8 – 20 mm |
>= 45 % |
|
~ 20 ° C |
|
|
|
|
|
60 – 100 mm |
>= 50 % |
|
~ 20 ° C |
|
|
|
|
|
20 – 60 mm |
>= 35 J |
|
~ 20 ° C |
|
|
|
|
1) |
100 – 160 mm |
>= 35 J |
|
~ 20 ° C |
|
|
|
|
1) |
|