Ürün Materyel No
1.7213
Ürün Adı
25CrMoS4

KİMYASAL BİLEŞİM

C Si Mn P S Cr Mo Ni V
0.22 – 0.29 max 0.4 0.6 – 0.9 max 0.025 0.02 – 0.04 0.9 – 1.2 0.15 – 0.3 0.00 0.00
Al Cu Pb N Ti Br Sc Bh Sn
0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00

STANDARTLARIN KARŞILAŞTIRILMASI

Avrupa
EURO
Almanya
DIN
Amerika
AISI-SAE
Fransa
AFNOR
İtalya
UNI
Çin
GB
Türkiye
TSE
25CrMoS4 25CrMoS4 25CrMoS4 25 CD 4 u 25CrMoS4 25CrMoS4 25CrMoS4
Mekanik Özellikler
hafif tavlı
16 – 40 mm 800 – 950 MPa ~ 20 ° C
100 – 160 mm 650 – 800 MPa ~ 20 ° C
16 – 40 mm >= 14 % ~ 20 ° C
100 – 160 mm >= 16 % ~ 20 ° C
16 – 40 mm >= 55 % ~ 20 ° C
100 – 160 mm >= 60 % ~ 20 ° C
40 – 100 mm >= 50 J ~ 20 ° C 1)
8 – 20 mm >= 600 MPa ~ 20 ° C 7)
60 – 100 mm >= 400 MPa ~ 20 ° C 7)
8 – 20 mm 800 – 950 MPa ~ 20 ° C
60 – 100 mm 650 – 800 MPa ~ 20 ° C
8 – 20 mm >= 14 % ~ 20 ° C
60 – 100 mm >= 16 % ~ 20 ° C
8 – 20 mm >= 55 % ~ 20 ° C
60 – 100 mm >= 60 % ~ 20 ° C
20 – 60 mm >= 50 J ~ 20 ° C 1)
~ 3 mm 43 – 52 HRC
~ 7 mm 37 – 50 HRC
~ 11 mm 32 – 46 HRC
~ 15 mm 27 – 41 HRC
~ 25 mm 21 – 35 HRC
~ 35 mm <= 32 HRC
~ 45 mm <= 31 HRC
~ 3 mm 46 – 52 HRC
~ 7 mm 41 – 50 HRC
~ 11 mm 37 – 46 HRC
~ 15 mm 32 – 41 HRC
~ 25 mm 26 – 35 HRC
~ 35 mm 23 – 32 HRC
~ 45 mm 22 – 31 HRC
~ 3 mm 43 – 49 HRC
~ 7 mm 37 – 46 HRC
~ 11 mm 32 – 41 HRC
~ 15 mm 27 – 36 HRC
~ 25 mm 21 – 30 HRC
~ 35 mm <= 28 HRC
~ 45 mm <= 27 HRC
5 – 40 mm <= 560 MPa
5 – 40 mm >= 62 %
5 – 40 mm <= 600 MPa
5 – 40 mm >= 60 %
5 – 40 mm <= 560 MPa
5 – 40 mm >= 62 %
5 – 40 mm <= 600 MPa
5 – 40 mm >= 60 %
Kangal
40 – 63 mm <= 212 HBW
40 – 63 mm >= 450 MPa 1)
40 – 63 mm 700 – 850 MPa 1)
40 – 63 mm >= 15 % 1)
40 – 63 mm >= 450 MPa 1)
40 – 63 mm 700 – 850 MPa 1)
40 – 63 mm >= 15 % 1)
10 – 16 mm <= 260 HBW
40 – 63 mm <= 250 HBW
10 – 16 mm >= 700 MPa 1)
40 – 63 mm >= 520 MPa 1)
10 – 16 mm 900 – 1,100 MPa 1)
2)
40 – 63 mm 700 – 900 MPa 1)
2)
10 – 16 mm >= 9 % 1)
40 – 63 mm >= 11 % 1)
63 – 100 mm >= 12 % 1)