Ürün Materyel No
1.7227
Ürün Adı
42CrMoS4

KİMYASAL BİLEŞİM

C Si Mn P S Cr Mo Ni V
0.38 - 0.45 max 0.4 0.6 - 0.9 max 0.025 0.02 - 0.04 0.9 - 1.2 0.15 - 0.3 0.00 0.00
Al Cu Pb N Ti Br Sc Bh Sn
0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00

STANDARTLARIN KARŞILAŞTIRILMASI

Avrupa
EURO
Almanya
DIN
Amerika
AISI-SAE
Fransa
AFNOR
İtalya
UNI
Çin
GB
Türkiye
TSE
42CrMoS4 4140 42CrMoS4 42 CD 4 u 42CrMoS4 42CrMoS4 42CrMoS4
Mekanik Özellikler
Yüzey Sertlik [HRC]
16 - 40 mm >= 750 MPa ~ 20 ° C 9)
100 - 160 mm >= 550 MPa ~ 20 ° C 9)
16 - 40 mm 1,000 - 1,200 MPa ~ 20 ° C
100 - 160 mm 800 - 950 MPa ~ 20 ° C
16 - 40 mm >= 11 % ~ 20 ° C
100 - 160 mm >= 13 % ~ 20 ° C
16 - 40 mm >= 45 % ~ 20 ° C
100 - 160 mm >= 50 % ~ 20 ° C
40 - 100 mm >= 35 J ~ 20 ° C 1)
160 - 250 mm >= 35 J ~ 20 ° C 1)
kesmeye hazır halde
8 - 20 mm >= 750 MPa ~ 20 ° C 9)
60 - 100 mm >= 550 MPa ~ 20 ° C 9)
8 - 20 mm 1,000 - 1,200 MPa ~ 20 ° C
60 - 100 mm 800 - 950 MPa ~ 20 ° C
8 - 20 mm >= 11 % ~ 20 ° C
60 - 100 mm >= 13 % ~ 20 ° C
8 - 20 mm >= 45 % ~ 20 ° C
60 - 100 mm >= 50 % ~ 20 ° C
20 - 60 mm >= 35 J ~ 20 ° C 1)
100 - 160 mm >= 35 J ~ 20 ° C 1)
Mekanik Özellikler
Çekirdek sertleşme testi
~ 3 mm 53 - 61 HRC
~ 7 mm 51 - 60 HRC
~ 11 mm 43 - 59 HRC
~ 15 mm 37 - 58 HRC
~ 25 mm 32 - 53 HRC
~ 35 mm 30 - 48 HRC
~ 45 mm 29 - 46 HRC
~ 3 mm 56 - 61 HRC
~ 7 mm 54 - 60 HRC
~ 11 mm 48 - 59 HRC
~ 15 mm 44 - 58 HRC
~ 25 mm 39 - 53 HRC
~ 35 mm 36 - 48 HRC
~ 45 mm 35 - 46 HRC
~ 3 mm 53 - 58 HRC
~ 7 mm 51 - 57 HRC
~ 11 mm 43 - 54 HRC
~ 15 mm 37 - 51 HRC
~ 25 mm 32 - 46 HRC
~ 35 mm 30 - 42 HRC
~ 45 mm 29 - 40 HRC
5 - 40 mm <= 610 MPa
5 - 40 mm >= 60 %
5 - 40 mm <= 650 MPa
5 - 40 mm >= 58 %
5 - 40 mm <= 610 MPa
5 - 40 mm >= 60 %
5 - 40 mm <= 650 MPa
5 - 40 mm >= 58 %
Kangal
40 - 63 mm <= 241 HBW
40 - 63 mm >= 650 MPa 2)
40 - 63 mm 900 - 1,100 MPa 2)
40 - 63 mm >= 12 % 2)
40 - 63 mm >= 650 MPa 2)
40 - 63 mm 900 - 1,100 MPa 2)
40 - 63 mm >= 12 % 2)
10 - 16 mm <= 290 HBW
40 - 63 mm <= 280 HBW
10 - 16 mm >= 750 MPa 2)
40 - 63 mm >= 650 MPa 2)
10 - 16 mm 1,000 - 1,200 MPa 1)
2)
40 - 63 mm 900 - 1,100 MPa 1)
2)
10 - 16 mm >= 8 % 2)
40 - 63 mm >= 10 % 2)
63 - 100 mm >= 10 % 2)