Ürün Materyel No
1.4568
Ürün Adı
X7CrNiAl17-7

KİMYASAL BİLEŞİM

C Si Mn P S Cr Mo Ni V
max 0.09 max 0.7 max 1 max 0.04 max 0.015 16 - 18 0.00 6.5 - 7.8 0.00
Al Cu Pb N Ti Br Sc Bh Sn
0.7 - 1.5 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00

STANDARTLARIN KARŞILAŞTIRILMASI

Avrupa
EURO
Almanya
DIN
Amerika
AISI-SAE
Fransa
AFNOR
İtalya
UNI
Çin
GB
Türkiye
TSE
X7CrNiAl17-7 631 X7CrNiAl17-7 Z 9 CNA 17-07 X7CrNiAl17-7 0Cr17Ni7Al X7CrNiAl17-7
Mekanik Özellikler
soğuk haddelenmiş şerit
>= 3 mm >= 2 % enine ~ 20 ° C 1)
3)
<= 3 mm >= 2 % enine ~ 20 ° C 1)
2)
3)
4)
<= 3 mm >= 2 % enine ~ 20 ° C 1)
3)
5)
Mekanik Özellikler
Barlar
>= 0.05 mm 600 - 800 MPa 9)
15)
>= 0.05 mm 800 - 1,000 MPa 11)
15)
>= 0.05 mm 1,000 - 1,250 MPa 2)
15)
>= 0.05 mm 1,200 - 1,450 MPa 4)
15)
>= 0.05 mm 1,600 - 1,900 MPa 6)
15)
1 - 3 mm <= 1,050 MPa ~ 20 ° C 1)
14)
5 - 16 mm <= 950 MPa ~ 20 ° C 1)
14)
1 - 3 mm >= 10 % ~ 20 ° C 14)
5 - 16 mm >= 15 % ~ 20 ° C 14)
>= 3 mm >= 19 % enine ~ 20 ° C 6)
<= 3 mm >= 19 % enine ~ 20 ° C 2)
4)
6)
<= 3 mm >= 19 % enine ~ 20 ° C 5)
6)
>= 3 mm >= 2 % enine ~ 20 ° C 1)
3)
<= 3 mm >= 2 % enine ~ 20 ° C 1)
2)
3)
4)
<= 3 mm >= 2 % enine ~ 20 ° C 1)
3)
5)
Mekanik Özellikler
Barlar
3 - 5 mm <= 1,000 MPa ~ 20 ° C 1)
3)
<= 30 mm <= 850 MPa ~ 20 ° C 4)
3 - 5 mm >= 10 % ~ 20 ° C 3)
1,150 - 1,300 MPa 2)
1,500 - 1,700 MPa 4)
0.2 - 0.3 mm >= 2,250 MPa 2)
3)
0.4 - 0.5 mm >= 2,200 MPa 2)
3)
0.65 - 0.8 mm >= 2,125 MPa 2)
3)
1 - 1.25 mm >= 2,050 MPa 2)
3)
1.5 - 1.75 mm >= 1,950 MPa 2)
3)
2 - 2.5 mm >= 1,850 MPa 2)
3)
3 - 3.5 mm >= 1,750 MPa 2)
3)
4.25 - 5 mm >= 1,650 MPa 2)
3)
6 - 7 mm >= 1,500 MPa 2)
3)
8.5 - 10 mm >= 1,500 MPa 2)
3)
0.2 - 0.3 mm 1,950 - 2,250 MPa 1)
4)
0.4 - 0.5 mm 1,900 - 2,190 MPa 1)
4)
0.65 - 0.8 mm 1,825 - 2,100 MPa 1)
4)
1 - 1.25 mm 1,750 - 2,020 MPa 1)
4)
1.5 - 1.75 mm 1,650 - 1,900 MPa 1)
4)
2 - 2.5 mm 1,550 - 1,790 MPa 1)
4)
3 - 3.5 mm 1,450 - 1,670 MPa 1)
4)
4.25 - 5 mm 1,350 - 1,560 MPa 1)
4)
6 - 7 mm 1,250 - 1,440 MPa 1)
4)
8.5 - 10 mm 1,250 - 1,440 MPa 1)
4)