Ürün Materyel No
1.4024
Ürün Adı
X15Cr13

KİMYASAL BİLEŞİM

C Si Mn P S Cr Mo Ni V
0.12 - 0.17 max 1 max 1 max 0.04 max 0.015 12 - 14 0.00 0.00 0.00
Al Cu Pb N Ti Br Sc Bh Sn
0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00

STANDARTLARIN KARŞILAŞTIRILMASI

Avrupa
EURO
Almanya
DIN
Amerika
AISI-SAE
Fransa
AFNOR
İtalya
UNI
Çin
GB
Türkiye
TSE
X15Cr13 420 X15Cr13 Z 12 C 13 M X15Cr13 1Cr13 X15Cr13
Mekanik Özellikler
Suverilmiş ve menevişlenmiş
<= 3 mm >= 15 % boyuna ~ 20 ° C 1)
2)
4)
<= 3 mm >= 15 % enine ~ 20 ° C 1)
2)
4)
<= 3 mm >= 15 % boyuna ~ 20 ° C 2)
5)
<= 3 mm >= 15 % enine ~ 20 ° C 2)
5)
>= 3 mm >= 20 % enine ~ 20 ° C
<= 3 mm >= 20 % enine ~ 20 ° C 1)
4)
<= 3 mm >= 20 % enine ~ 20 ° C 5)
>= 3 mm >= 20 % enine ~ 20 ° C
<= 3 mm >= 20 % enine ~ 20 ° C 1)
4)
<= 3 mm >= 20 % enine ~ 20 ° C 5)
>= 410 MPa ~ 150 ° C 2)
>= 385 MPa ~ 250 ° C 2)
>= 300 MPa ~ 400 ° C 2)
>= 410 MPa ~ 150 ° C 2)
>= 385 MPa ~ 250 ° C 2)
>= 300 MPa ~ 400 ° C 2)
>= 410 MPa ~ 150 ° C 2)
>= 385 MPa ~ 250 ° C 2)
>= 300 MPa ~ 400 ° C 2)
>= 410 MPa ~ 150 ° C 2)
>= 385 MPa ~ 250 ° C 2)
>= 300 MPa ~ 400 ° C 2)
<= 160 mm >= 450 MPa ~ 20 ° C 2)
3)
Gerilme direnci
boyut değer numunenin konumu sıcaklığı
<= 160 mm 650 - 850 MPa ~ 20 ° C 2)
3)
Kırık sonrası uzama (A 5,65)
boyut değer numunenin konumu sıcaklığı
<= 160 mm >= 15 % boyuna ~ 20 ° C 2)
3)